Niobium Addition in Cr-Mo-1/4V Steel Castings for Steam Turbine Casing Applications

ABSTRACT

A chromium-molybdenum-vanadium (Cr—Mo—V) cast steel including 0.04 to 0.08% by weight of niobium is disclosed. The cast steel may include 0.08 to 0.12% by weight carbon. The cast steel may also have a sulphur content of 0.015% by weight or less, and a phosphorus content of 0.02% by weight or less. The silicon content may be 0.30 to 0.60% by weight, the manganese content may be 0.50 to 0.80% by weight, the chromium content may be 1.20 to 1.50% by weight, the molybdenum content may be 0.90 to 1.10% by weight, and the vanadium content may be 0.20 to 0.30% by weight.

FIELD OF THE INVENTION

This invention relates to steel casting containing Niobium.

This invention further relates to chromium-Molybdenum-Vanadium steel castings containing Niobium, for use in steam turbine casing or valve casing applications.

BACKGROUND OF THE INVENTION

To improve the mechanical properties and weldability of steels, various alloying elements such as Ti, Nb, Mo, W, B etc. have been added to low and high alloy steels. Ti and Nb are added as carbide formers and strengthen the alloy steels by forming fine matrix carbides which interact with dislocations and precipitate at subgrain boundaries thus reducing the secondary creep rate.

Presently base CrMoV steel castings are being used for turbine casing and valve casting applications up to around 540° C. Due to increase in power demand and limitation on CO₂ emission, there is increasing demand for higher efficiency and output of the stem turbines. It is possible by increasing the temperature and pressure of the turbine without much increase in cost.

OBJECTS OF THE INVENTION

It is therefore an object of this invention to propose a chromium-Molybdenum-Vanadium cast steel containing Nb, having greater mechanical strength and ductility at ambient and high temperatures and pressures.

It is a further object of this invention is to propose a chromium-Molybdenum-vanadium cast steel containing Nb, having greater creep rupture time, rupture Elongation and reduction of area under high temperature.

Another object of this invention to propose a chromium-Molybdenum-vanadium cast steel containing Nb, which can be used for manufacturing turbine casings or other components which are subjected to high temperatures and pressures.

SUMMARY OF THE INVENTION

According to this invention is provided a chromium-molybdenum-vanadium cast steel containing niobium. More particularly, the invention provides a heat resistant chromium-molybdenum vanadium steel consisting essentially of 0.08 to 0.12% by weight of carbon, 0.015% by weight or less of sulphur, 0.02% by weight or less of phosphorous, 0.30 to 0.60% by weight of silicon, 0.50 to 0.80% by weight of manganese, 1.20 to 1.50% by weight of chromium, 0.90 to 1.00% by weight of molybdenum, 0.20 to 0.30 by weight of vanadium, the balance being iron apart from incidental impurities, with niobium ranging from 0.04 to 0.08% by weight.

BRIEF DESCRIPTION OF THE ACCOMPANYING DRAWINGS

The invention will now be explained in greater details with the help of the accompanying drawings where:

FIG. 1: Schematic diagram showing the double ‘V’ edge used for preparation of weld joints

FIG. 2: Sampling plan for qualification of welding procedures

FIG. 3: Larson Miller Parameter vs. stress plots for 1Cr1Mo1/4V steel weld joints with different Nb contents.

FIG. 4: Larson Miller Parameter vs. stress plots for 1Cr1Mo1/4V steel weld joints with different Nb contents.

FIG. 5: Larson Miller Parameter vs. elongation plots for 1Cr1Mo1/4V steel with different Nb contents.

FIG. 6: Larson Miller parameter vs. elongation plots for 1Cr1Mo1/4 steel weld joints with different Nb.

FIG. 7: Effect of Nb content on creep-rupture properties of 1Cr1Mo1/4 V steel tested at different test conditions.

FIG. 8: Effect of Nb content on creep-rupture properties of 1Cr1Mo1/4V steel tested at 200 Mpa at different test temperatures.

DESCRIPTION OF THE INVENTION

According to this invention is provided a chromium-molybdenum-vanadium (Cr—Mo—V) cast steel containing 0.04 to 0.08% by weight of Niobium.

The cast steel contains 0.08 to 0.12% by weight of carbon, 0.015% by weight or less of sulphur, 0.02% by weight or less of phosphorus, 0.30 to 0.60% by weight of silicon, 0.50 to 0.80% by weight of manganese, 1.20 to 1.50% by weight of chromium, 0.90 to 1.00% by weight of molybdenum, 0.20 to 0.30 by weight of vanadium, the balance being iron apart from incidental impurities with 0.04 to 0.08% by weigh Niobium being added. The base chromium molybdenum-vanadium cast steel is subjected to a homogenizing heat treatment of cast steel, followed by addition of Niobium in percentages of 0.04 to 0.08 by weight. The Nb addition is carried out in an induction melting furnace.

The casts containing Niobium, thus a prepared have been subjected to various tests to evaluate their creep/stress rupture, tensile strength.

Three casts were obtained by adding Nb in 0.4 to 0.8% to CrMoV steel. The steel melts were designated as cast ‘B’, cast ‘C’ and cast ‘D’ respectively. The base melt without Nb is designated as cast ‘A’.

A: Base chromium-molybdenum-vanadium cast (CrMov cast)

B: CrMoV cast with 0.04% by weight of Niobium.

C: CrMoV cast with 0.06% Niobium.

D: CrMoV cast with 0.08% Niobium

The heat treatment for cast ‘A’ was carried out by solutionising base CrMoV steel by holding for 3 hours at 940° C. followed by forced air cooling. The other casts ‘B’, ‘C’ and ‘D’ were heat treated by solutionising the CrMoVNb steel by holding for 3 hours at 1040° C. followed by forced air cooling. Subsequently all the casts were tempered at 740° C. for 5 hours and cooled up to 300° C. in the furnace and then air cooled to room temperature.

The compositions of all four casts are provided in Table—1.

TABLE 1 Chemical composition of 1Cr1Mo1/4 V castings with different Nb Heat No. C S P Si Mn Cr Mo V Nb Al Cu Ni A 0.11 0.018 0.020 0.45 0.57 1.40 1.00 0.25 <0.01 0.050 B 0.12 0.010 0.026 0.50 0.60 1.40 1.00 0.28 0.04 0.02 0.010 C 0.12 0.020 0.024 0.50 0.55 1.47 0.98 0.27 0.06 0.02 0.030 D 0.12 0.010 0.012 0.53 0.51 1.70 1.03 0.24 0.08 0.019 Specified 0.08-0.12 0.015 0.02 0.30-0.60 0.50-0.80 1.20-1.50 0.90-1.10 0.20-0.30 max max Permissible ±0.02 ±0.003 ±0.003 ±0.10 ±0.07 ±0.08 ±0.06 ±0.03 Variation Heat No Co Ti W Pb Sn As Bi Ce Sb B A 0.005 0.003 0.01 <0.001 <0.001 0.001 <0.001 B <0.001 <0.001 0.01 <0.001 <0.001 <0.001 <0.001 C <0.001 <0.001 0.01 <0.001 <0.001 <0.001 <0.001 D <0.001 <0.001 0.01 <0.001 <0.001 <0.001 <0.001

CrMoV electrodes were used for welding. Welding, as per the plant practices detailed out in table 2, was carried out on the castings to get the adequate number of samples. Weldability studies were conducted. Weldability tests with 1800 bend test passed on all the four casts.

TABLE 2 Details of the Welding procedures: Preheat temperature 300° C.(Validity: 240° C. Min) Inter-pass Temp. 400° C. (Valifity: 500° C. Max) State of heat treatment Quenched & Tempered Type of Post weld heat Treatment Quenching and Tempering Temp. WQ-930° C.(valid from 930° C. to 950° C.) T-720° C. (valid from 710° C. to 730° C.) Time WQ-6 Hours T-8 Hours. Current range 180-220 Amp. DC Voltage range 24-28 V Polarity Reverse (valid for DCEP Only) Joint Preparation Full penetration with backing Location of Weld Root face 2 mm, Root gap 5 mm, seam side angle 10° Weld sequence Multilayer Welding

All the four casts of CrMoV steel without and with niobium (Nb addition were subjected to hardness, impact, tensile, hot tensile and creep/stress rupture testing. Creep/stress rupture testing were carried out at 525, 550, 575 and 600° C. and stresses varying from 100-300 MPa. Microstructural analysis including scanning electron microscopy was carried out on the as received as well as creep rupture tested material.

Room and high temperature tensile strength of 1Cr1Mo1/4V steel with Nb addition was tested and is higher than plain 1Cr1Mo1/4V steel. Among Nb added steels, tensile strength of 0.06% Nb steel was found to be highest. 1Cr1Mo1/4V castings with 0.06% and 0.08% Nb exhibit higher creep rupture properties (FIG. 3). The creep ductility of these casts is slightly lower than plain 1Cr1Mo1/4V steel.

On the basis of creep-rupture test results on weld joint samples, the weld joints of steel with 0.06% Nb are found to be stronger than plain 1Cr1Mo1/4V steel as well as with 0.04 and 0.08% Nb (Tables 3 & 4 & FIGS. 3 to 8)

TABLE 3 Room temperature tensile strength of CrMoV steel castings Condition UTS YS % EL % RA Remarks Longitudinal direction Cast A 62.79 42.70 20.80 58.19 Without Nb 64.18 45.00 22.28 67.06 Cast B 72.30 60.00 19.88 63.18 73.36 60 19.08 62.12 Cast C 73.29 61.14 19.02 58.79 74.47 61.79 18.00 59.68 Cast D 73.92 62.50 18.74 63.81 72.62 61.10 16.45 65.51 Transverse direction Cast A 64.95 45.9 24.11 65.70 Cast B 72.15 60.10 17.14 60.38 Cast C 73.19 60.7 18.57 60.38 Cast D 73.52 62.10 17.14 60.48

TABLE 4 Impact strength of CrMoV steels Impact strength of base metal in longitudinal direction, J Cast A 20J 16J 32J 43J Cast B 27J 23J 51J 28J Cast C 39J 21J 50J 26J Cast D 54J 62J 35J 30J Impact strength of base metal in transverse direction, J Cast A 43J 40J 36J Cast B 24J 22J 20J Cast C 25J 32J 35J Cast D 24J 35J 31J Impact strength of the weld joint, J Cast A AW1-50J AW2-48J AW4-56J Cast B BW1-36J BW2-45J BW4-34J Cast C CW3-34J CW4-33J CW5-29J Cast D DW1-29J DW3-36J DW5-36J Impact strength of the HAZ, J Cast A AH1-85J AH2-66J AH5-91J Cast B BH3-44J BH4-76J BH5-42J Cast C CH2-22J CH4-36J CH5-41J Cast D DH1-54J DH3-73J DH4-65J

The castings with Nb content exhibit excellent mechanical and creep properties at high temperature. If a turbine casing is made of Nb containing steels, it is possible to increase the steam temperature and pressure. The weldability of the steel also increases, which will help in repair jobs. 

1-8. (canceled)
 9. A chromium-molybdenum-vanadium (Cr—Mo—V) cast steel comprising 0.04 to 0.08% by weight of niobium.
 10. The Cr—Mo—V cast steel according to claim 9, further comprising a carbon content of 0.08 to 0.12% by weight.
 11. The Cr—Mo—V cast steel according to claim 9, further comprising a sulphur content of 0.015% by weight or less.
 12. The Cr—Mo—V cast steel according to claim 9, further comprising a phosphorous content of 0.02% by weight or less.
 13. The Cr—Mo—V cast steel according to claim 9 further comprising a silicon content of 0.30 to 0.60% by weight.
 14. The Cr—Mo—V cast steel according to claim 9, further comprising a manganese content of 0.50 to 0.80% by weight.
 15. The Cr—Mo—V cast steel according to claim 9, further comprising a chromium content of 1.20 to 1.50% by weight.
 16. The Cr—Mo—V cast steel according to claim 9, further comprising a molybdenum content of 0.90 to 1.10% by weight.
 17. The Cr—Mo—V cast steel according to claim 9, further comprising a vanadium content of 0.20 to 0.30% by weight. 